Effect of commercial silanes on bond strength of resin cement to lithium disilicate ceramic / Efeito de silanos comerciais na resistência de união do cimento resinoso à cerâmica de dissilicato de lítio

The aim of this study was to evaluate the effect of different commercial silanes on microshear bond strength of resin cement to lithium disilicate ceramic. Twenty ceramic samples with 10 mm in length, 10 mm wide and 3 mm in thickness were fabricated, etched with 10% hydrofluoric acid for 20 seconds, and divided into 5 groups, according to the commercial silane applied: G1- RelyX Ceramic Primer (3M ESPE), G2- Angelus Silane, G3- Prosil (FGM), G4- Dentsply Silane (Dentsply) and G5- Bis-Silane (Bisco). Silanes were applied in accordance to manufacturers' recommendations. Addition silicone molds with 1 mm in thickness, 10 mm in diameter and 3 perforations with 1 mm in diameter each one, were placed on ceramic and filled with the resin cement RelyX ARC (3M ESPE) in all groups. Light activation was performed with LED Bluephase G2 (Ivoclar Vivadent) at 1200 mW/cm2, for 30 seconds. Samples were maintained in 100% humidity at 37°C for 24 hours and submitted to microshear test. The data (MPa) were submitted to one-way ANOVA and Tukey test (α=0.05). The results obtained for each group were: G1: 22.39±2.99; G2: 23.35±4.08; G3: 26.05±5.46; G4: 18.56±4.09; G5: 25.26±4.10. Statistical analysis showed significantly lower microshear bond strength for G4. Fracture pattern analysis showed predominance of adhesive failures in G1 and G2. G3 and G5 presented higher percentage of cohesive failures in ceramic, and G4 showed mixed, adhesive and cohesive fractures with similar percentages. It was concluded that different silanes showed influence on the lithium disilicate ceramic ­ resin cement bond strength

O objetivo neste estudo foi avaliar o efeito de diferentes silanos comerciais na resistência de união ao microcisalhamento do cimento resinoso à cerâmica de dissilicato de lítio. Foram confeccionadas 20 amostras de cerâmica (10mm de comprimento, 10mm de largura e 3mm de espessura), condicionadas com ácido fluorídrico a 10% por 20 segundos e divididas em 5 grupos, de acordo com o silano aplicado: G1- RelyX Ceramic Primer (3M ESPE), G2- Silano Angelus, G3-Prosil (FGM), G4- Silano Dentsply e G5-Bis-Silane (Bisco). Matrizes de silicone por adição (1 mm de espessura, 10 mm de diâmetro e 3 perfurações com 1 mm de diâmetro) foram colocadas sobre a cerâmica e preenchidas com cimento resinoso RelyX ARC (3M ESPE). A fotoativação foi realizada com LED Bluephase G2 (Ivoclar Vivadent) a 1200 mW/cm2, por 30 segundos. As amostras foram mantidas em 100% de umidade a 37°C por 24 horas e submetidas ao teste de microcisalhamento. Os dados (MPa) (G1: 22,39+2,99; G2: 23,35+4,08; G3: 26,05+5,46; G4: 18,56+ 4,09; G5: 25,26+4,10) foram submetidos a análise de variância e ao teste de Tukey (p<0,05). A análise estatística mostrou valor de resistência de união significantemente menor para G4. A análise do padrão de fratura mostrou predominância de falha adesiva para G1 e G2. G3 e G5 apresentaram maior porcentagem de falha coesiva em cerâmica, e o G4 apresentou fraturas mista, adesiva e coesiva em igual porcentagem. Concluiu-se que os diferentes silanos apresentaram influência na resistência de união do cimento resinoso à cerâmica de dissilicato de lítio

Bond strength and marginal microleakage in restorations photopolymerized with LED and halogen light associated with three application modes of a universal adhesive system: in vitro study / Resistência de união e da microinfiltração marginal em restaurações fotopolimerizadas com LED e luz halógena associadas a três modos de aplicação de um sistema adesivo universal: estudo in vitro

ABSTRACT Objective: This study aimed to assess the bond strength and marginal microleakage in composite resin restorations, using the Single Bond Universal adhesive system associated with Ultralux (halogen) and Bluephase (LED) light curing units. Methods: For bond strength, 80 healthy human third molars were divided into halogen light (n=40) and LED (n=40), and subdivided according to the following application techniques for the adhesive system: etch-and-rinse (enamel), self-etching (enamel), etch-and-rinse (dentin), and self-etching (dentin). The teeth were subjected to the microtensile test and the fracture pattern was observed under an optical microscope at 40X magnification; they were analyzed by ANOVA, and Fisher and Tukey's tests (5%). For the marginal microleakage test, 120 class II cavities were prepared in 60 healthy human third molars that were randomly divided into halogen light (n=30) and LED (n=30), and subdivided according to the following application techniques for the adhesive system: etch-and-rinse, selective etching, and self-etching. The teeth were thermocycled 2000 times (±5/55°C), stained in 5% basic fuchsin and sectioned for qualitative and quantitative assessments; they were analyzed by Kruskall-Wallis and Dunn tests (5%). Results: For the bond strength of enamel and dentin, the adhesive application with prior acid etching was better than self-etching (p<0.0001), regardless of the type of light curing unit (p<0.05). Etch-and-rinse showed the lowest microleakage values (p<0.0001). Conclusion: Etch-and-rinse obtained the best results relative to the other application techniques for the adhesive system in both tests, regardless of the type of light curing unit.

RESUMO Objetivo: Avaliar a resistência de união e microinfiltração marginal em restaurações de resina composta, utilizando sistema adesivo Single Bond Universal associado com fotoativadores Ultralux (halógeno) e Bluephase (LED). Métodos: Para resistência de união, oitenta terceiros molares humanos hígidos foram divididos: Halógena (n=40); LED (n=40), sendo subdivididos de acordo com a técnica de aplicação do sistema adesivo: condicionamento total-esmalte; autocondicionante-esmalte; condicionamento total-dentina; autocondicionante-dentina. Os dentes foram submetidos ao teste de microtração e o padrão de fratura foi observado em microscópio ótico - 40X de aumento, analisadas pelos testes ANOVA, Tukey e Fisher (5%). Para o ensaio de microinfiltração marginal, 120 cavidades classe II foram preparadas em sessenta terceiros molares humanos hígidos, aleatoriamente divididos: Halógena (n=30); LED (n=30) e subdivididos de acordo com a técnica de aplicação do sistema adesivo: condicionamento total; condicionamento seletivo; autocondicionante. Os dentes foram termociclados 2000 vezes (±5/55ºC), corados em fucsina básica 5% e seccionados para avaliações qualitativa e quantitativa, analisados pelos testes Kruskall-Wallis e Dunn (5%). Resultados: Para resistência de união em esmalte e dentina, a aplicação do adesivo com condicionamento ácido prévio, foi melhor que o autocondicionante (p<0.0001), independentemente do tipo de fotoativador utilizado (p<0.05). O condicionamento total mostrou os menores valores de microinfiltração, (p<0.0001). Conclusão: O condicionamento total, obteve os melhores resultados em relação às outras técnicas de aplicação do sistema adesivo em ambos os testes, independentemente do tipo de aparelho fotoativador.

In vitro evaluation of the antibacterial behavior of a self-etch adhesive associated with chlorhexidine / Avaliação in vitro da ação anti-bacteriana de um adesivo auto-condicionante acrescido de clorexidina

Abstract Introduction Adhesive technology has been developed quickly since its introduction about fifty years ago. Its goal is to produce a close contact within enamel and dentin. Failures in this process could result in microleakage, and allow the infiltration of bacteria, fluids and ions. Recent studies have been shown the use of chlorhexidine associated with adhesive systems can be able to inhibit the bacteria action. Objective The aim of this study was to evaluate the addiction of different percentages of chlorhexidine to a self-etch adhesive. Methodology The solution of digluconatechlorhexidine was increased to the primer of the two pass self etch adhesive to create a 0.5%, 1.0% and 2.0% chlorhexidine primer solution and after they were distributed in four groups (G1, G2, G3 and G4). Saliva samples (N=10) were used to test bacteria activity. Result They were spread in a blood medium with filter paper disks containing the different treatments. After the incubation, the inhibitions halos formation were evaluated. Conclusion This study demonstrated that, in vitro, the addition of different percentages of chlorhexidine digluconate to the self-etch adhesive induced inhibited halos at bacteria of saliva samples, independent from their concentration.

Resumo Introdução A tecnologia adesiva vem se desenvolvendo rapidamente desde que foi introduzida há mais de 50 anos. O principal objetivo da adesão é alcançar um íntimo contato entre a estrutura dental e o material restaurador e fornecer adequada união entre o esmalte e a dentina. Objetivo A proposta deste estudo foi avaliar o efeito antibacteriano de um adesivo auto-condicionante de dois passos associado a diferentes concentrações de solução de digluconato de clorexidina (DCHX). Metodologia A solução de digluconato de clorexidina a 20% foi adicionada ao primer do sistema adesivo nas concentrações de 0,5, 1,0 e 2,0% e distribuídas em quatro grupos (G1, G2, G3 e G4). Para o teste de atividade antibacteriana foram utilizadas amostras de saliva (N=10) semeadas em meio de ágar sangue e discos de papel filtro contendo os diferentes grupos. Após incubação, as amostras foram inspecionadas quanto à formação de halo de inibição dos microrganismos através da utilização do paquímetro digital de precisão (0,0001mm) (Mitutoyou Sul Americana Ltda/ Starret Tools ®). Resultado Halos de inibição foram encontrados ao redor de todos os discos de filtro em que foram aplicados o primer acrescido de clorexidina mais o adesivo, bem como ao redor dos discos do controle positivo. Ao redor dos discos do controle negativo e dos discos com primer e adesivo não modificado não foram observados halos de inibição. Conclusão Este trabalho demonstrou que, in vitro, a adição de diferentes concentrações de digluconato de clorexidina ao sistema adesivo produziu halo de inibição dos microrganismos presentes nas amostras de saliva, independente da concentração utilizada.

Restaurações cerâmicas multicamadas e monolíticas: uma revisão de literatura / Multilayered and monolithic ceramic restorations: a literature review

Objetivo: realizar uma revisão de literatura sobre materiais, técnicas de confecção, vantagens, desvantagens e limitações das restaurações cerâmicas multicamadas e monolíticas. Revisão de literatura: embora as cerâmicas odontológicas sejam utilizadas para confecção de restaurações dentárias indiretas, porque têm excelentes propriedades mecânicas e estéticas, são materiais susceptíveis à fratura sob forças oclusais. Para compensar essa fragilidade, restaurações multicamadas são confeccionadas associando um material mais resistente para a infraestrutura e a posterior aplicação de cerâmica para recobrimento estético. Porém, as restaurações multicamadas apresentam como desvantagem o possível lascamento da cerâmica de recobrimento. Essas falhas comprometem a restauração funcional e a estética, exigindo a substituição da peça protética em muitos casos. Sendo assim, devido à evolução de sistemas cerâmicos e técnicas de processamento, surgiram as restaurações cerâmicas monolíticas fabricadas com um único material, a fim de superar tal limitação. Nesse sentido, diferentes materiais e técnicas são apresentados na literatura para a confecção de restaurações cerâmicas monolíticas. Considerações finais: as restaurações multicamadas têm bom resultado estético, porém podem apresentar lascamento da cerâmica de recobrimento. Essa limitação é superada pelo uso de um único material para as restaurações monolíticas, mas o resultado estético pode ser limitado. De um modo geral, a literatura demonstra um bom comportamento clínico para as restaurações cerâmicas multicamadas e monolíticas, quando a técnica de confecção e o sistema cerâmico são bem indicados. (AU)

Objective: the aim of this study was to conduct a literature review about the materials, techniques, advantages, disadvantages and limitations of multilayer and monolitic ceramic restorations. Literature review: although dental ceramics have been used for fabrication of dental restorations due to its good esthetic and mechanical properties, it is a material prone to fracture under oclusal loading. To surpass such fragility, multilayer restorations are fabricated using a resistant framework material associated to esthetic veneering ceramic. However, multilayer restorations present risk to chipping of veneering ceramic. Those failures represent a functional and esthetic problem, leading to restoration replacement. So, the evolution of ceramic systems and techniques generated monolitic restorations using a single material. Several materials and techniques are presented in the literature for fabrication of monolitic ceramic restorations. Final considerations: multilayer restorations present good esthetic result but delamination of veneering ceramic can occur. Such limitation is solved using a single material in monolitic restorations, but esthetic result is limited. In general, literature shows appropriate clinical performance for both multilayer and monolitic ceramic restorations when technique and materials are well indicated. (AU)

The influence of three photoactivation techniques on the sorption and solubility of different composite resins / A influência de três técnicas de fotoativação na sorção e solubilidade de diferentes resinas compostas

Introduction: There is a growing demand for aesthetic restorations and the polymerized composite resins are the most used material in these procedures. In order to achieve greater resistance to solubilization proper polymerization is required. Objective: Evaluate the influence of three photoactivation techniques, on sorption and solubility of three composite resins. Materials and methods: 90 test samples measuring 8 mm diameter and 1 mm thick were made and divided into 9 groups (n=10) of resins -Filtek Z350 XT, Tetric N-Ceram and IPS Empress Direct, each of them was polymerized with LED Bluephase, using the techniques: Conventional, Soft-Start (SS) and Pulse Delay (PD). Afterwards they were placed in desiccator with silica gel at 98.6 F and weighed daily until obtaining a constant mass (m1). Then they were immersed in deionized water for seven days and weighed again (m2). The test sample reconditioning was performed using the m1 procedure, until a constant mass (m3 ) was obtained. The sorption and solubility values were calculated and subjected to ANOVA test (two-way), followed by Tukey post hoc, p<0.05. Result: There were no statistically significant differences in sorption and solubility among the studied resins when photoactivation techniques were compared. For solubility analysis, statistically significant differences were observed among the materials. The results for composite resin Filtek Z350 XT presented higher statistical hybridization values than those of the other evaluated resins. Conclusion: The different forms of photoactivation had no influence on the sorption and solubility of the tested composite resins.

Introdução: Há uma crescente demanda por restaurações estéticas, sendo as resinas compostas polimerizadas o material mais utilizados nesses procedimentos. Visando uma maior resistência à solubilização, uma polimerização adequada é necessária. Objetivo: Avaliar a influência de três técnicas de fotoativação na sorção e na solubilidade de três resinas compostas. Material e método: Foram confeccionados 90 corpos-de-prova, com 8 mm de diâmetro e 1 mm de espessura, divididos em 9 grupos (n = 10) de resinas - Filtek Z350 XT, Tetric N-Ceram e IPS Empress Direct, cada uma elas polimerizada com LED Bluephase, utilizando as técnicas: Convencional, Soft-Start (SS) e Pulse Delay (PD). Posteriormente foram colocadas em dessecador com sílica gel a 98,6 F e pesadas diariamente até obtenção de massa constante (m1). Depois foram imersos em água desionizada durante sete dias e pesados ​​novamente (m2). O recondicionamento da amostra de teste foi realizado utilizando o procedimento m1, até que uma massa constante (m3) fosse obtida. Os valores de sorção e solubilidade foram calculados e submetidos ao teste ANOVA (two-way), seguido por Tukey post hoc, p <0,05. Resultado: Não houve diferenças estatisticamente significantes para sorção e solubilidade nas resinas estudadas quanto as técnicas de fotoativação. Para análise de solubilidade, foram observadas diferenças estatisticamente significantes entre os materiais. Os resultados para resina compostaFiltek Z350 XT apresentaram valores de hibridação estatísticos superiores aos das outras resinas compostas avaliadas. Conclusão: As diferentes formas de fotoativação não influenciaram a sorção e solubilidade das resinas compostas testadas.

Influência da solução de irrigação sobre a resistência adesiva de um cimento resinoso de dupla polimerização / Influence of solution of irrigation on the resistance of and adhesive resin cement double polymerization

Objetivo: Avaliar a influência de diferentes soluções de irrigação cavitária sobre a resistência de união de um cimento resinoso de dupla polimerização. Material e Método: A partir de incisivos bovinos, foram obtidos 4 grupos (n=15), divididos aleatoriamente de acordo com a solução irrigadora empregada na limpeza cavitária, sendo: G0 - soro fisiológico + condicionamento ácido; G1 ­ EDTA + condicionamento ácido; G2 - Clorexidina 2% + condicionamento ácido + clorexidina 2% e G3 - soro fisiológico + condicionamento ácido + clorexidina 2%. Foram confeccionados cilindros de cimento resinoso para cada coroa, utilizando-se uma matriz de Tygon com diâmetro interno de 1 mm e altura de 2 mm. O teste de resistência adesiva por microcisalhamento foi realizado após 3 meses de armazenamento dos espécimes em soro fisiológico a 37ºC. Os dados foram submetidos ao teste de Kruskall-Wallis, seguido do teste de Dunn (p<0,05). Resultados: Os grupos G0, G1 e G3 não apresentaram diferenças significativas entre si (p>0,05). Os menores valores foram observados no grupo G2 (p<0,05). Conclusões: As soluções irrigadoras EDTA e soro fisiológico utilizadas previamente ao condicionamento ácido da dentina não interferiram, significativamente, na resistência de união, porém, a solução de clorexidina utilizada após o condicionamento ácido influenciou negativamente nos valores de resistência de união.

Objectives: This study aimed to evaluate the influence of different cavity irrigation solutions on the bond strength of a dual-curing resin cement. Methods: From bovine incisors, 4 groups (n=15), were randomly divided according to the irrigating solution for cavity cleaning: G0 ­ saline + acid etching; G1 ­ EDTA + acid etching; G2: Chlorhexidine 2% + acid etching + Chlorhexidine 2%; and G3 ­ Saline + acid etching + Chlorhexidine 2%. Resin cement cylinders were made for each crown, using a Tygon matrix with internal diameter of 1 mm and height of 2 mm. The specimens were stored for 3 months at 37oC, and then subjected to microshear tests. Data were statistically analyzed by Kruskal-Wallis test followed by Dunn (p<0.05). Results: There were no statistically significant differences between G0, G1 and G3 groups (p>0.05). The lowest values were observed in G2 group (p<0.05). Conclusion: The irrigation solutions EDTA and saline used before to the acid etching of dentin did not interfere, significantly, in the bond strength, however, the solution of chlorhexidine used after the acid etching influenced negatively.

Clinical Evaluation of Class I Restorations Made with Composite with Low Degree of Polymerization Shrinkage.

Aims: The objective of this study was to clinically evaluate the performance of a conventional resin system and one with low polymerization shrinkage. Study Design: A prospective, randomized, blind, split-mouth study. Place and Duration of Study: Dental Clinic, division of Heath Sciencies, State University of West Parana - UNIOESTE/Brazil, between October, 2011 and October, 2012. Methodology: Teeth were restored with one of the two tested materials (n = 10): Conventional composite resin restorations (CCR) and Silorane-based resin composite restorations (SCR). The materials were used according to manufacturer’s instructions. After time intervals of 30 days, 6 months and 1 year, the restorations were assessed using the USPHS criteria. The data obtained were tabulated and evaluated by the Chi-square test for clinical parameters and for the restoration criteria (p< 0.05). Results: No statistically significant differences between the two composite resins were found, with exception of marginal adaptation, in which CCR showed better results than SCR. Conclusion: The silorane-based composite resin showed no advantage over the methacrylate resin.

Avaliação da influência da solução de irrigação na resistência adesiva de um cimento resinoso / Evaluation of influence of irrigation solution in strength adhesive of a resin cement

Introdução: A contaminação do substrato dentinário pode interferir na qualidade de união entre materiais adesivos e o dente. Objetivo: Investigar a influência de diferentes soluções de irrigação na resistência de união de um cimento resinoso. Material e Método: Foram selecionadas 40 coroas dentais bovinas, divididas em quatro grupos: G0 = soro; G1 = clorexidina; G2 = EDTA; G3 = clorexidina 0,12%, após condicionamento ácido. Em seguida, foram confeccionados cilindros de cimento resinoso utilizando-se uma matriz de Tygon com diâmetro interno de 1 mm e 2 mm de altura. A fotoativação foi realizada por aparelho de luz LED com 900 mW/cm² por 40 segundos. Foram confeccionados quatro cilindros de cimento resinoso para cada coroa bovina, totalizando 40 corpos de prova de cimento resinoso para cada grupo avaliado. O teste de resistência adesiva por microcisalhamento foi realizado após 24 horas. Decorrido esse período, os cilindros de cimento resinoso foram testados em uma máquina universal de ensaios (EMIC). Os dados obtidos foram submetidos à análise estatística pelos testes ANOVA e Tukey (p = 0,001). Resultado: Não houve diferenças estatisticamente significativas entre os grupos estudados, com exceção para o G3, que apresentou de forma significativa os menores valores de resistência adesiva. Conclusão: As diferentes soluções irrigadoras utilizadas previamente ao condicionamento ácido na dentina não interferem na resistência de união por microcisalhamento.

Introduction: The contamination of dentin can interfere with the quality of union between adhesives and tooth. Objective: Was to investigate the influence of different irrigation solutions on bond strength of a resin cement. Material and Method: Were selected 40 dental bovine crowns divided into four groups: G0= physiologic serum, G1= chlorhexidine, G2= EDTA, G3= 0.12% chlorhexidine after acid etching. Then the cylinders were fabricated resin cement using a matrix of Tygon with an internal diameter of 1mm and 2mm in height. The polymerization was carried out by LED light unit with 900 mW/cm² for 40 seconds. 4 cylinders were made of resin cement for each bovine crown, totaling 40 body-of-proof resin cement for each group evaluated. The test microshear bond strength was performed after 24 hours. After this period, the resin cement cylinders were tested in a universal testing machine (EMIC). Data were statistically analyzed by ANOVA and Tukey (p = 0.001). Result: There were no statistically significant differences between groups, except for the G3 which showed significantly lower values of bond strength. Conclusion: The different irrigating solutions used prior to etching dentin not interfere in the bond strength microshear.

Avaliação da sorção e solubilidade de uma resina composta em diferentes meios líquidos / Sorption and solubility assessment of a resin composite in different liquids

Este trabalho avaliou a sorção e a solubilidade de uma resina composta nanoparticulada em três meios líquidos diferentes: água destilada, Coca-Cola® e etanol/água a 75%, em função de dois períodos de armazenamentos: 7 e 15 dias. Foram confeccionados 30 espécimes, acondicionados em sílica gel azul, desidratada a 37°C, por 24 horas. Em seguida, foram pesados em balança analítica de precisão, repetindo-se até que se obtivesse massa constante (m1). Com a obtenção da m1, os espécimes foram subdivididos em 6 grupos e armazenados na solução. Três grupos permaneceram por 7 dias, e os outros três, por 15 dias. Após o período de armazenamento, os espécimes foram removidos, lavados, secos, pesados para a obtenção de uma segunda medida de massa, denominada m2. Os espécimes foram, então, recondicionados em estufa a 37°C. Mensurações de massa foram realizadas durante a desidratação, a cada 24 horas, obtendo-se a m3. Os dados de sorção e solubilidade foram calculados e submetidos à análise estatística. A resina nanoparticulada mostrou-se resistente à degradação química em meio ácido e em meio aquoso, mas foi suscetível à degradação, quando imerso em solução de etanol/água a 75%, apresentando solubilidade, sem diferença estatística entre os períodos de armazenamento.

This study evaluated the sorption and solubility of resin composite nanoparticle in three different liquid : distilled water, Coca-Cola ® and ethanol / water at 75%, according two periods of stores: 7 and 15 days. We prepared 30 specimens, packed in plastic container containing silica gel blue dehydrated and taken to an incubator at 37 ° C for 24 hours. Following, we weighed in analytical balance, and repeated until achieving constant mass (m1) on every 24 hour period. By getting the m1, the specimens were been divided into six groups and stored separately in 5 mL of each solution. Three groups were been maintained for 7 days and the other three for 15 days. After the storage period, the specimens were removed, washed, dried, weighed to obtain a second measure of mass, called m2. The specimens was reconditioned at 37 ° C. Mass measurements were performed during dehydration, every 24 hours, getting the dough reconditioned, with constant value of mass, called m3. The Data from sorption and solubility, we calculated and subjected to statistical analysis. The composite resin Filtek Z350 was found to be resistant to chemical degradation in acid and aqueous, but was susceptible to degradation when immersed in a solution of ethanol / water at 75%, with solubility, no statistical difference between the periods of storage.

Planejamento estético do sorriso: relato de caso clínico / Planning the esthetic smile: a case report

A beleza e a harmonia das restaurações odontológicas estão controladas por alguns fatores que servem de parâmetros e auxiliam na reconstrução de um sorriso, a estes fatores chamamos de princípios estéticos. O objetivo deste trabalho foi descrever um caso clínico elucidando os principais princípios estéticos e ao mesmo tempo observando que estãotodos interligados para a obtenção de um resultado estético satisfatório. Foi possível concluir com este relato de caso clínico, a devolução da harmonia do sorriso sobre o ponto de vista estético e funcional.

The beauty and harmony of dental restorations are controlled by several factors that serve as parameters and help in the reconstruction of a smile, and these factors are called esthetic principles. The aim of this study was to describe a clinical case elucidating the main esthetic principles, and at the same time, observe that they are all interconnected in order to obtain a satisfactory esthetic result. Through this Clinical Case Report it was possible to conclude restoration of the harmony of the smile from the esthetic and functional points of view.

Estudo da precisão dimensional de modelos de gesso confeccionados com diferentes técnicas e materiais de moldagem elastoméricos / Study of dimensional accuracy of stone models made with different techniques and elastomeric impression materials

Objetivo: O objetivo este estudo foi mensurar e comparar a precisão dimensional de modelos de gesso confeccionados por meio de três técnicas de moldagem (técnicado reembasamento, dupla mistura e moldeira individual), com seis diferentes marcas comerciais de elastômeros (Express®, Futura AD®, Clonage®, Silon APS®, Optosil/Xantopren® e Zetaplus/Oranwash®). Métodos: Inicialmente, foi obtido um modelo metálico padrão simulando uma arcada inferior com pontos de referêncianos dentes 33 (CE), 43 (CD), 37 (ME) e 47 (MD), que foi utilizado para a realização das moldagens. Foram medidas as distâncias entre os dentes CD-CE, MD-ME, MECE e MD-CD. Após os procedimentos de moldagem e confecção dos corpos-de-prova, os modelos foram avaliados num microscópio comparador com aumentode 30x e os valores das distâncias, analisados estatisticamente por meio da análise de variância com dois fatores,sendo as médias comparadas pelo teste de Tukey (5 por cento). Resultados e Conclusão: Os dados demonstraramque os silicones polimerizados por adição foram os materiais que mostraram melhores resultados de precisão dimensional, ao passo que os silicones polimerizados por condensação apresentaram os piores resultados. Não foram encontradas diferenças entre as três técnicasde moldagem

Tratamento superficial de cerâmicas reforçadas in-ceram previamente aos procedimentos de cimentação adesiva: revisão de literatura / Superficial treatment of the reinforced in ceram ceramic before the luting procedures: literature review

Desde o início do emprego das cerâmicas em restaurações indiretas, a odontologia passou a viver uma nova realidade. Na busca pelo aperfeiçoamento desses materiais surgiram as coroas protéticas de cerâmicas reforçadas por vidro, que possuem maior resistência à fratura, porém apresentam dificuldades no condicionamento superficial prévio aos procedimentos cimentadores. Objetivando apontar um protocolo de condicionamento superficial e de cimentação adesiva deste tipo de material, o presente trabalho traz uma revisão de literatura acerca das diferentes técnicas de tratamento de superfície interna de coroas protéticas de cerâmicas reforçadas por vidro. Os principais métodos empregados e que merecem ser discutidos são os jateamentos com óxido de alumínio e partículas de sílica, bem como a palicação de ácido fluorídrico e a silanização. Atualmente, as pesquisas têm apontado para a silicatização como o meio mais eficiente para prover a retenção entre este tipo de material e o remanescente dentário, quando procedimentos de cimentação adesiva são empregados. Os cimentos que possuem monômeros fosfatados também apresentam evidências de serem mais efetivos neste tipo de cimentação e têm sido indicados com sucesso.

Influência da luz de cura Diferentes Unidades de Resistência de União de restaurações de resina Composta indireta

O Objetivo Deste estudo da UM Foi avaliar Influência de Diferentes fontes de luz Sobre a Resistência adesiva de resina Composta de restaurações indiretas cimentadas com cimento resinoso dual hum . A dentina superficial de Terceiros molares Humanos Foi exposto e ácido - Gravado e hum Sistema Adesivo Foi aplicado (Single Bond 2 ). Quatro mm de espessura de resina Composta de restaurações indiretas ( GRADIA ) foram confeccionadas e cimentadas com cimento resinoso UM dual (Rely X). Quatro fontes de luz Foram utilizados Parágrafo polimerizar o cimento : QTH - Optilux 401; LED1 - LEDemetron 1; LED2 - Optilight CL e LED3 - Ultralume 5. Os dentes Por armazenados Foram 24 horas e seccionados , produzindo espécimes em forma de n com Bastão grupo CADA área aderida de 1,0 mm ². Os espécimes Foram então testados em Uma Máquina Universal de Ensaios , a Uma Velocidade de 1 mm / min. Os Dados Foram analisados Usando ANOVA. Bond Força Os valores médios foram: QTH : 22,5 (± 8,4 ); LED1 : 22,7 (± 9,4 ); LED2 : 21,4 (± 10,2 ) e 27,3 LED3: (± 13,8 ). Não Houve diferença estatisticamente significativa Entre os Grupos experimentais . A resistência de União Valores QUANDO o cimento com Diferentes Foi Luzes LED polimerizada Foram equivalentes EAo QUANDO valores de Uma luz QTH Foi Utilizada . Pode-se concluir Que A variedade de fontes de luz Não Utilizadas presente estudo , Não influenciou Uma Resistência de União de resina Composta de restaurações indiretas cimentadas com cimento resinoso dual Zumbido

Influence of different light curing units on the bond strength of indirect resin composite restorations

The aim of this study was to evaluate the influence of different light sources on the bond strength of indirect resin composite restorations cemented with a dual-cure resin cement. The superficial dentin of human third molars was exposed and acid-etched and an adhesive system was applied (Single Bond 2). Four-mm-thick indirect resin composite restorations (Gradia) were fabricated and cemented using a dual-cure resin cement (Rely X). Four light sources were used to polymerize the cement: QTH - Optilux 401; LED1 - L.E.Demetron 1; LED2 - Optilight CL; and LED3 - Ultralume 5. The teeth were stored for 24 h and then sectioned, yielding stick-shaped specimens for each group with a bonded area of 1.0 mm². The specimens were then tested in a universal testing machine, at a crosshead speed of 1 mm/min. Data were analyzed using ANOVA. Bond strength mean values were: QTH: 22.5 (± 8.4); LED1: 22.7 (± 9.4); LED2: 21.4 (± 10.2); and LED3: 27.3 (± 13.8). No statistically significant difference was observed among the experimental groups. The bond strength values when the cement was polymerized using different LED lights were equivalent to the values when the QTH light was used. It can be concluded that the variety of light sources used in the present study did not influence the bond strength of indirect resin composite restorations cemented with a dual-cure resin cement.

Avaliação dos sistemas de retenção para overdentures implanto suportadas mandibulares: revisão de literatura / Arresting systems evaluation of for overdentures I implant supported mandibular: literature revision

O objetivo deste trabalho foi efetuar uma revisão da literatura sobre overdentures mandibulares, desde a sua origem e inter-relação da prótese total com os implantes osseointegrados; níveis de sucesso nas reabilitações; números de implantes necessários para retenção e estabilização; comparação entre os sistemas de retenção barra-clipe, bola e magneto; e qualidade de vida após a reabilitação com overdentures implanto retidas.

Prótese total pela técnica da zona neutra / Total prótese for the technique of the neutral zone

O uso da técnica da zona neutra tem demonstrado bastante eficiência clínica, principalmente em prótese total mandibular, onde a reabsorção do rebordo apresenta-se bastante grande. Esta técnica permite distribuir os dentes artificiais, de forma adequada biomecanicamente em relação ao rebordo alveolar e à musculatura paraprotética, proporcionando assim, melhores resultados estéticos, fonéticos e maior facilidade de adaptação. Como esta técnica proporciona maior conforto ao paciente, o grau de satisfação em relação ao tratamento é maior.

Pinos intradentinários em dente polpado: relato de caso / Dental pins in vital tooth: case report

A reabilitação bucal tem como premissa básica, sempre que for possível, a preservação dos tecidos bucais. Desta forma, este relato de caso clínico vem adicionar informações sobre as vantagens da utilização de um material restaurador, classificado como compômero, indicado para a confecção de núcleo de reconstrução e da utilização de pinos intradentinários. No caso clínico descrito, foi confeccionada uma prótese parcial fixa de três elementos, tendo como pilares o segundo molar inferior direito e o segundo pré-molar inferior e como pôntico o primeiro pré-molar inferior direito ausente. Optou-se pela confecção de um núcleo de reconstrução no dente 47, que se mostrou com importante perda de estrutura dental, porém com saúde pulpar, e além disso a utilização de pinos intradentinários e canaletas de retenção, que foram capazes de proporcionar retenção satisfatória e resistência à peça protética, respeitando os conceitos de preservação do tecido remanescente. A utilização da combinação dos materiais e procedimentos descritos possibilitou a preservação pulpar do elemento 47, conferindo características anatômicas à coroa, dando, desta forma, condições biomecânicas para manter a prótese fixa em função e, ainda, minimizando o custo e o tempo de trabalho, sem qualquer prejuízo da qualidade.